Long-term Comparison of Bond Strength Between One/Two Bottle and Self/ Total-Etch Universal Adhesive Systems
Journal of Dental School, Shahid Beheshti University of Medical Sciences,
Vol. 38 No. 1 (2020),
21 April 2021
,
Page 14-19
https://doi.org/10.22037/jds.v38i1.30796
Abstract
Objectives The aim of this study was to compare the shear bond strength and durability of one/two-bottle All-Bond Universal used in self-etch (SE) and total-etch (TE) modes on dentin discs.
Methods In this in vitro study, 144 human premolars were allocated to 12 groups for use of one-bottle or two-bottle adhesive in SE and TE modes and their assessment at three time points. Dentin discs with 2 mm thickness were prepared. They were polished with 600 and 800 grit silicon carbide abrasive papers. One/two-bottle All-Bond Universal bonding agent was used in SE and TE modes in the groups. Composite resin cylinders were made by the Tygon tubes on the bonding surface and then cured . Shear bond strength was measured by a universal testing machine at 24 h, and 6 and 12 months, and the mode of failure was determined under a stereomicroscope at x10 magnification. Data were analyzed by two-way ANOVA and Bonferroni test.
Results After 24 h and 6 and 12 months, the micro-shear bond strength was significantly lower in one-bottle SE compared with other groups. The two-bottle TE group showed the highest bond strength (P<0.001). In all groups, the bond strength significantly decreased at 12 months, compared with 24 h (P<0.05).
Conclusion Two-bottle TE system showed higher bonding durability and bond strength compared with other groups.
- Shear Strength
- Dental Bonding
- Materials Testing
How to Cite
References
Daneshkazemi P, Ghasemi A, Daneshkazemi A, Shafiee F. Evaluation of micro shear bonding strength of two universal dentin bondings to superficial dentin by self etch and etch-and-rinse strategies.J Clin Exp Dent. 2018;10(9):e837-43.
Steiner R, Edelhoff D, Stawarczyk B, Dumfahrt H, Lente I. Effect of Dentin Bonding Agents, Various Resin Composites and Curing Modes on Bond Strength to Human Dentin. Materials (Basel). 2019;12(20):3395.
Cuevas-Suárez CE, de Oliveira da Rosa WL, Lund RG, da Silva AF, Piva E. Bonding Performance of Universal Adhesives: An Updated Systematic Review and Meta-Analysis. J Adhes Dent. 2019;21(1):7-26.
Oz FD, Ergin E, Canatan S. Twenty-four-month clinical performance of different universal adhesives in etch-and-rinse, selective etching and self-etch application modes in NCCL–a randomized controlled clinical trial. J Appl Oral Sci. 2019;27:e20180358..
Perdigao J, Loguercio AD. Universal or multi-mode adhesives: why and how? J Adhes Dent. 2014;16(2):193-4.
Emamieh S, Sadr A, Ghasemi A, Torabzadeh H, Akhavanzanjani V, Tagami J. Effects of solvent drying time on mass change of three adhesives. Journal of conservative dentistry: J Conserv Dent. 2013;16(5):418-22.
Hattan MA, Pani SC, AlOmari M. Composite bonding to stainless steel crowns using a new universal bonding and single-bottle systems.Int J Dent. 2013;2013:607405.
Kim RJ-Y, Woo J-S, Lee I-B, Yi Y-A, Hwang J-Y, Seo D-G. Performance of universal adhesives on bonding to leucite-reinforced ceramic.Biomater Res. 2015;19:11.
Marchesi G, Frassetto A, Mazzoni A, Apolonio F, Diolosa M, Cadenaro M, et al. Adhesive performance of a multi-mode adhesive system: 1-year in vitro study.J Dent. 2014;42(5):603-12.
Kaczor K, Gerula‐Szymańska A, Smektała T, Safranow K, Lewusz K, Nowicka A. Effects of different etching modes on the nanoleakage of universal adhesives: A systematic review and meta‐analysis. J Esthet Restor Dent. 2018;30(4):287-98.
Sadr A, Shimada Y, Tagami J. Effects of solvent drying time on micro-shear bond strength and mechanical properties of two self-etching adhesive systems.Dent Mater. 2007;23(9):1114-9.
Cardoso GC, Nakanishi L, Isolan CP, Jardim PDS, Moraes RR.. Bond Stability of Universal Adhesives Applied To Dentin Using Etch-And-Rinse or Self-Etch Strategies.Braz Dent J. 2019;30(5):467-75.
.Elkaffas AA, Hamama HH, Mahmoud SH. Do universal adhesives promote bonding to dentin? A systematic review and meta-analysis.Restor Dent Endod. 2018;43(3):e29.
Ye Q, Park J, Topp E, Wang Y, Misra A, Spencer P. In vitro performance of nano-heterogeneous dentin adhesive. J Dent Res. 2008;87(9):829-33.
Bahrololumi N, Beglou A, Najafi-Abrandabadi A, Sadr A, Sheikh-Al-Eslamian S-M, Ghasemi A. Effect of water storage on ultimate tensile strength and mass changes of universal adhesives. J Clin Exp Dent. 2017;9(1):e78-83.
Reis A, Wambier L, Malaquias T, Wambier DS, Loguercio AD. Effects of warm air drying on water sorption, solubility, and adhesive strength of simplified etch-and-rinse adhesives. J Adhes Dent. 2013;15(1):41-6.
Cruz J, Sousa B, Coito C, Lopes M, Vargas M, Cavalheiro A. Microtensile bond strength to dentin and enamel of self-etch vs. etch-and-rinse modes of universal adhesives. Am J Dent. 2019;32(4):174-82.
Emamieh S, Sadr A, Ghasemi A, Torabzadeh H, Akhavanzanjani V, Tagami J. Effects of solvent drying time and water storage on ultimate tensile strength of adhesives. J Investig Clin Dent. 2014;5(1):51-7.
Asande Adebayo O, Francis Burrow M, John Tyas M. Bonding of one-step and two-step self-etching primer adhesives to dentin with different tubule orientations. Acta Odontol Scand. 2008;66(3):159-68.
Xie C, Han Y, Zhao X, Wang Z, He H. Microtensile bond strength of one-and two-step self-etching adhesives on sclerotic dentin: the effects of thermocycling. Oper Dent. Sep-Oct 2010;35(5):547-55.
Dey S, Shenoy A, Kundapur S, Das M, Gunwal M, Bhattacharya R. Evaluation of the effect of different contaminants on the shear bond strength of a two-step self-etch adhesive system, one-step, self-etch adhesive system and a total-etch adhesive system. J Int Oral Health 2016; 8(3):378-384.
Takamizawa T, Barkmeier WW, Tsujimoto A, Berry TP, Watanabe H, Erickson RL, et al. Influence of different etching modes on bond strength and fatigue strength to dentin using universal adhesive systems. Dent Mater. 2016;32(2):e9-21.
Seabra B, Arantes-Oliveira S, Portugal J. Influence of multimode universal adhesives and zirconia primer application techniques on zirconia repair. J Prosthet Dent. 2014;112(2):182-7.
Saikaew P, Fu J, Chowdhury AA, Carvalho RM, Sano H. Effect of air-blowing time and long-term storage on bond strength of universal adhesives to dentin. Clin Oral Investig. 2019;23(6):2629-35.
Saito T, Takamizawa T, Ishii R, Tsujimoto A, Hirokane E, Barkmeier W, et al. Influence of Application Time on Dentin Bond Performance in Different Etching Modes of Universal Adhesives. Oper Dent. 2020;45(2):183-95.
Sarr M, Benoist FL, Bane K, Aidara AW, Seck A, Toure B. Bonding effectiveness of self-etch adhesives to dentin after 24 h water storage. J Conserv Dent. 2018;21(2):142-6.
Tian F, Zhou L, Zhang Z, Niu L, Zhang L, Chen C, et al. Paucity of nanolayering in resin-dentin interfaces of MDP-based adhesives. J Dent Res. 2016;95(4):380-7.
Lee J, Cho K-Y, Kim J-Y, Park S, Roh B-D, Shin Y. Bonding effectiveness of different dentin conditions on etch-and-rinse mode of two universal adhesives: the confocal laser scanning and shear bond strength. J Adhes Sci Technol. 2017;31(9):933-42.
Makishi P, André C, Ayres A, Martins A, Giannini M. Effect of storage time on bond strength and nanoleakage expression of universal adhesives bonded to dentin and etched enamel. Oper Dent. 2016;41(3):305-17.
Knobloch LA, Gailey D, Azer S, Johnston WM, Clelland N, Kerby RE. Bond strengths of one-and two-step self-etch adhesive systems. J Prosthet Dent. 2007;97(4):216-22.
Taschner M, Nato F, Mazzoni A, Frankenberger R, Falconi M, Petschelt A, et al. Influence of preliminary etching on the stability of bonds created by one‐step self‐etch bonding systems. Eur J Oral Sci. 2012;120(3):239-
Belli R, Sartori N, Peruchi LD, Guimarães JC, Araújo É, Monteiro Jr S, et al. Slow progression of dentin bond degradation during one-year water storage under simulated pulpal pressure. J Dent. 2010;38(10):802-10.
Mena‐Serrano A, Kose C, De Paula EA, Tay LY, Reis A, Loguercio AD, et al. A new universal simplified adhesive: 6‐month clinical evaluation. J Esthet Restor Dent. 2013;25(1):55-69.
Ma S, Fujita K, Nishiyama N. Effects of storage temperature on the shelf life of one-step and two-step self-etch adhesives. Oper Dent. 2009;34(4):472-80.
Ahmed MH, Yoshihara K, Mercelis B, Van Landuyt K, Peumans M, Van Meerbeek B. Quick bonding using a universal adhesive. Clin Oral Investig. 2020;24(8):2837-51.
Abdalla AI, ElSayed HY, Garcia-Godoy F. Effect of hydrostatic pulpal water pressure on microtensile bond strength of self-etch adhesives to dentin. Am J Dent. 2008;21(4):233-8.
Nishitani Y, Yoshiyama M, Donnelly A, Agee K, Sword J, Tay F, et al. Effects of resin hydrophilicity on dentin bond strength. J Dent Res. 2006;85(11):1016–21.
Aldrighi Münchow E, Zanchi CH, Aulo Ogliari F, Gonçalves Souza e Silva M, Rubin de Oliveira I, Piva E. Replacing HEMA with alternative dimethacrylates in dental adhesive systems: evaluation of polymerization kinetics and physicochemical properties. J Adhes Dent. 2014;16(3):221-8.
Yoshida K, Tsuo Y, Atsuta M. Bonding of dual‐cured resin cement to zirconia ceramic using phosphate acid ester monomer and zirconate coupler. J Biomed Mater Res B Appl Biomater. 2006;77(1):28-33.
Ye Q, Spencer P, Wang Y, Misra A. Relationship of solvent to the photopolymerization process, properties, and structure in model dentin adhesives. J Biomed Mater Res A. 2007;80(2):342-50.
Luque-Martinez IV, Perdigão J, Muñoz MA, Sezinando A, Reis A, Loguercio AD. Effects of solvent evaporation time on immediate adhesive properties of universal adhesives to dentin. Dent Mater. 2014;30(10):1126-35.
.Muñoz MA, Luque I, Hass V, Reis A, Loguercio AD, Bombarda NHC. Immediate bonding properties of universal adhesives to dentine. J Dent. 2013;41(5):404-11.
Blosser R, Bowen R. Effects of purified ferric oxalate/nitric acid solutions as a pretreatment for the NTG-GMA and PMDM bonding system. Dent Mater. 1988;4(5):225-31.
Tay FR, Pashley DH, Suh BI, Carvalho RM, Itthagarun A. Single-step adhesives are permeable membranes. J Dent.2002;30(7-8):371-82.
- Abstract Viewed: 181 times
- PDF Downloaded: 117 times