Effect of triple antibiotic paste and calcium hydroxide as intracanal medicaments on bond strength of composite to dentin
Journal of Dental School,
Vol. 33 No. 2 (2015),
25 April 2015
,
Page 169-174
https://doi.org/10.22037/jds.v33i2.24741
Abstract
Objective: Considering the use of triple antibiotic paste (TAP) for root canal treatment of open apex teeth, this study aimed to assess the effect of TAP and calcium hydroxide (CH) on bond strength of composite to dentin.
Methods: This in-vitro study was conducted on 32 extracted human premolar teeth. After disinfection with 2% thymol solution, the enamel on the buccal surface of specimens was removed to expose a smooth dentin surface parallel to the long axis of the teeth with approximately 19mm2 surface areas. Specimens were divided into three groups of 11, 10 and 11 specimens. In group one, TAP, in group two CH and in group three, saline solution were applied to dentin surfaces for 14 days. After removal of medicaments, composite cylinders were bonded to the dentin surfaces using a bonding agent. Shear bond strength was measured in an Instron machine at a crosshead speed of 1mm/min. Data were analyzed using one-way ANOVA.
Results: The highest mean bond strength belonged to the control group (14.4760 MPa) and the lowest belonged to the TAP group (11.5808 MPa). The mean bond strength in CH group was less than that of the control and higher than that of the TAP group (11.7834 MPa). However, the difference among the three groups was not statistically significant (p=0.327).
Conclusion: Use of medicaments such as CH and TAP has no effect on bond strength of composite to dentin.
- Calcium hydroxide
- Composite
- Shear bond strength
- Triple antibiotic paste
How to Cite
References
Didier Dietschi, Serge Bouillaguet, Avishai Sadan: Restoration of the endodontically treated tooth.In:Cohen S, Hargreaves NM. Pathways of the pulp. 10thEd. St. Louis: The C. V. Mosby Co. 2011; Chap 22: 777-807.
Shafiei F, Memarpour M. Effect of chlorhexidine application on long-term shear bond strength of resin cements to dentin. J Prosthodont Res 2010; 54: 153-158.
Cvek M, Cleaton-Jones P, Austin J, Lownie J, Kling M, Fatti P. Effect of topical application of doxycycline on pulp revascularization and periodontal healing in reimplanted monkey incisors. Endod Dent Traumatol 1990; 6: 170-176.
Cvek M, Cleaton-Jones P, Austin J, Lownie J, Kling M, Fatti P. Pulp revascularization in reimplanted immature monkey incisors--predictability and the effect of antibiotic systemic prophylaxis. Endod Dent Traumatol 1990; 6: 157-169.
Kling M, Cvek M, Mejarel. Rate and predictability of pulp revascularization in therapeutically reimplanted permanent incisors. Endod Dent Traumatol 1986; 2: 83-89.
Yassen GH, Chu TM, Eckert G, Platt JA. Effect of medicaments used in endodontic regeneration technique on the chemical structure of human immature radicular dentin: an in vitro study. J Endod 2013; 39: 269-273.
Samanthini MV, Lata DA, Bharati Deo. Influence of endodontic materials on the bonding of composite resin to dentin –an in vitro study. JIDA 2011; 5: 605-608.
Katalinić I, Glockner K, Anić I. Influence of several root canal disinfection methods on pushout bond strength of self-etch post and core systems. Int Endod J 2014; 47: 140-146
Guneser MB, Akbulut MB, Eldeniz AU. Effect of various endodontic irrigants on the push-out bond strength of biodentine and conventional root perforation repair materials. J Endod 2013; 39: 380-384.
Renovato SR, Santana FR, Ferreira JM, Souza JB, Soares CJ, Estrela C. Effect of calcium hydroxide and endodontic irrigants on fiber post bond strength to root canal dentin. Int Endod J 2013; 46: 38-746
Norwich AH, Figdor D, Messer HH. PH changes in root dentin following calcium hydroxide intracanal dressing. Australian Endodontic Newsletter 1993; 19: 30-31.
Windley W 3rd, Ritter A, Trope M. The effect of short term calcium hydroxide treatment on dentin bond strength to composite resin. Dent Traumatol 2003; 19: 79-84.
Feiz A, Khoroushi M, Gheisarifar M. Effect of sodium ascorbate & calcium hydroxide on shear bond strength of composite resin to bleached enamel. JIDA 2009; 21: 115-121.
Mortazavi V, Khademi A, Khosravi K, Fathi MH, Ebrahimi-chaharom M, Shahnaseri SH, et al. Effect of MTAD on the shear bond strength of self etch adhesives to dentin. Dent Res J (Isfahan) 2012; 9: 24-30.
- Abstract Viewed: 200 times
- PDF Downloaded: 143 times