Effect of Er:YAG Laser and Reduced Time of Acid Etching on Bond Strength of Self-adhesive Resin Cement to MTA and Biodentine Bond Strength of Pretreated MTA and Biodentine
Journal of Lasers in Medical Sciences,
Vol. 12 (2021),
13 February 2021
,
Page e36
Abstract
Introduction: Considering the recent trend to use mineral trioxide aggregate (MTA) and Biodentine and resin cements, more conservative approaches concurrent with adequate bond strength have always been requested. The present study aimed to evaluate the effect of pretreatment with Er: YAG laser etching versus acid-etching for 5 and 15 seconds on the micro shear bond strength of selfadhesive resin cement (SRC) to MTA and Biodentine.
Materials and Methods: Forty-eight samples of each cement (MTA and Biodentine) were prepared and distributed into four groups based on surface pretreatment: 1) control, no treatment; 2) Er: YAG laser etching with the energy of 60 mJ; 3) 5-second acid-etching; 4) 15-second acid-etching. All specimens were cemented using SRC. Microshear bond strengths were tested following 24-hour water storage. Debonded specimens were examined and surface topography was assessed using an atomic force machine (AFM). Data analysis was performed using the two-way ANOVA and Tukey multiple comparisons test.
Results: The three testing groups of laser etch and 5-s and 15-s acid-etch demonstrated a significantly higher SBS than the control group (P<0.05) with negligible differences among them (P > 0.05). Furthermore, Biodentine showed better adhesive bonding than MTA in all groups.
Conclusion: Laser etching of 60 mJ and 5-s acid-etching were as beneficial as 15-s acid-etching in terms of bond strength of SRC to MTA and Bodentine.
- Acid-etching, Bond strength, Biodentine, Lasers, Mineral trioxide aggregate Angelus, Self-adhesive resin cement
How to Cite
References
Kang CM, Sun Y, Song JS, Pang NS, Roh BD, Lee CY, Shin Y. A randomized controlled trial of various MTA materials for partial pulpotomy in permanent teeth. J Dent. 2017;60:8-13.
Rajasekharan S, Martens LC, Cauwels RG, Verbeeck RM. Biodentine material characteristics and clinical applications: a review of the literature. Eur Arch Paediatr Dent. 2014;15(3):147-158.
Taha N, Ahmad M, Ghanim A. Assessment of mineral trioxide aggregate pulpotomy in mature permanent teeth with carious exposures. Int Endod J. 2017;50(2):117-125.
Spitznagel FA, Horvath SD, Guess PC, Blatz MB. Resin bond to indirect composite and new ceramic/polymer materials: a review of the literature. J Esthet Restor Dent. 2014;26(6):382-393.
Anadioti E, Aquilino SA, Gratton DG, Holloway JA, Denry IL, Thomas GW, Qian F. Internal fit of pressed and computer-aided design/computer-aided manufacturing ceramic crowns made from digital and conventional impressions. J Prosthet Dent. 2015;113(4):304-309.
Tabassum S, Khan FR. Failure of endodontic treatment: The usual suspects. Eur J Dent. 2016;10(1):144-147.
Manso AP, Carvalho RM. Dental Cements for Luting and Bonding Restorations: Self-Adhesive Resin Cements. Dent Clin North Am. 2017;61(4):821-834.
Mushashe AM, Gonzaga CC, Cunha LF, Furuse AY, Moro A, Correr GM. Effect of Enamel and Dentin Surface Treatment on the Self-Adhesive Resin Cement Bond Strength. Braz Dent J. 2016;27(5):537-542.
Rodrigues RF, Ramos CM, Francisconi PA, Borges AFS. The shear bond strength of self-adhesive resin cements to dentin and enamel: an in vitro study. J Prosthet Dent. 2015;113(3):220-227.
Pisani-Proenca J, Erhardt MC, Amaral R, Valandro LF, Bottino MA, Del Castillo-Salmeron R. Influence of different surface conditioning protocols on microtensile bond strength of self-adhesive resin cements to dentin. J Prosthet Dent. 2011;105(4):227-235.
Pavan S, dos Santos PH, Berger S, Bedran-Russo AK. The effect of dentin pretreatment on the microtensile bond strength of self-adhesive resin cements. J Prosthet Dent. 2010;104(4):258-264.
Shafiei F, Jowkar Z, Hosseini N. Influence of Cavity Pretreatments on the Fracture Resistance of Premolars with Self-adhesive Cemented Composite Inlay. J Contemp Dent Pract. 2019;20(7):829.
Shafiei F, Doozandeh M, Gharibpour F, Adl A. Effect of reducing acid-etching duration time on compressive strength and bonding of a universal adhesive to calcium silicate cements. Int Endod J. 2018.
Shafiei F, Dehghanian P, Memarpour M, Sabeti M. Effect of Er: YAG laser etching on topography, microstructure, compressive strength, and bond strength of a universal adhesive to calcium silicate cements. Clin oral investig. 2020;24(2):711-718.
Simundic Munitic M, Bago I, Glockner K, Kqiku L, Gabric D, Anic I. Effect of Different Laser Treatments on the Bond Strength of Intracanal Fiber Posts Cemented with a Self-Adhesive Resin Cement. J Prosthodont. 2018.
Nagakane K, Yoshida Y, Hirata I, Fukuda R, Nakayama Y, Shirai K, Ogawa T, Suzuki K, Van Meerbeek B, Okazaki M. Analysis of chemical interaction of 4-MET with hydroxyapatite using XPS. Dent Mater J. 2006;25(4):645-649.
Camilleri J. Scanning electron microscopic evaluation of the material interface of adjacent layers of dental materials. Dent Mater. 2011;27(9):870-878.
Lemos Martins Sicuro S, Gabardo MC, Castiglia Gonzaga C, Dias Morais N, Baratto-Filho F, Correr Nolasco GM, Leonardi DP. Bond Strength of Self-adhesive Resin Cement to Different Root Perforation Materials. J Endod. 2016;42(12):1819-1821.
Lee S-R, Moon Y-M, Hwang S-J, Seo M-S. The effect of acid-etch procedure on the bond between composite resin and mineral trioxide aggregate. 대한치과재료학회지. 2014;41(1):53-57.
Bodanezi A, Carvalho N, Silva D, Bernardineli N, Bramante CM, Garcia RB, Moraes IGd. Immediate and delayed solubility of mineral trioxide aggregate and Portland cement. J Appl Oral Sci. 2008;16(2):127-131.
Hashem DF, Foxton R, Manoharan A, Watson TF, Banerjee A. The physical characteristics of resin composite–calcium silicate interface as part of a layered/laminate adhesive restoration. Dent Mater. 2014;30(3):343-349.
Yoshida Y, Nagakane K, Fukuda R, Nakayama Y, Okazaki M, Shintani H, Inoue S, Tagawa Y, Suzuki K, De Munck J. Comparative study on adhesive performance of functional monomers. J Dent Res. 2004;83(6):454-458.
- Abstract Viewed: 696 times
- PDF Downloaded: 377 times