Effect of Air Abrasion and Erbium-Doped Yttrium Aluminum Garnet (Er: YAG) laser preparation on Shear Bond Strength of Composite to Dentin
Journal of Lasers in Medical Sciences,
Vol. 4 No. 3 (2013),
22 June 2013
,
Page 127-130
Abstract
Introduction: The aim of this study was to assess shear bond strength of composite to dentin after air abrasion and laser treatment.
Methods: 40 human extracted molars divided into 4 groups (n=10) received the following treatments. Group 1: carbide bur, Group 2: air abrasion with aluminum oxide 50 μm, Group 3: irradiated with Erbium-Doped Yttrium Aluminum Garnet (Er: YAG) laser (150 mJ/20Hz), Group 4: irradiated with Er:YAG laser (150 mJ/20Hz)+ air. Specimens in all groups were chemically etched with phosphoric acid 37% and treated with bonding agent (single bond 3M). Then, composite build-up was performed by tygon tube. After storage in distilled water at 37°c for one week, all specimens were subjected to a shear bond strength test with universal testing machine. Data were analyzed with ANOVA and T-Test.
Results: The mean and standard deviation of shear bond strength of the 4 groups were 20.8±6.76, 14.98±3.98, 11.43±4.36 and 14.95± 3.18 MPa, respectively.
Conclusion: Air abrasion after laser treatment improved the shear bond strength.
- Er-YAG laser
- dental air abrasion
- dentin
How to Cite
References
Bagramian RA, Garcia-Godoy F, Volpe AR. The global increase in dental caries; a pending public crisis. Am J Dent 2009; 22: 3-8
Antunes LA, Pedro RL, Viera AS, Maia LC. Effectiveness of high speed instrument air abrasion on different dental
subtracts. Braz Oral Res 2008; 22: 235-41
De Moor RJG, Delmé KIM, Laser-assisted Cavity Preparation and Adhesion to Erbium-lased Tooth Structure: Part 1. Laser-assisted Cavity Preparation, J Adhes Dent 2009; 11: 427-38.
Christensen GJ. Cavity preparation: cutting or abrasion? J Am Dent Assoc 1996; 127:1651-4.
Shahabi S, Chiniforush N, Juybanpoor N. Morphological Changes of Human Dentin after Erbium-Doped Yttrium Aluminum Garnet (Er:YAG) and Carbon Dioxide (CO2) Laser Irradiation and Acid-etch Technique: An scanning electron microscopic (SEM) Evaluation. J Lasers Med Sci 2013; 4(1):48-52.
Shahabi S, Chiniforush N, Bahramian H, Monzavi A, Baghalian A, Kharazifard MJ. The effect of erbium family laser on tensile bond Strength of composite to dentin in comparison with conventional method. Lasers Med Sci. 2013;28(1):139-42.
Delmé K, Meire M, De Bruyne M, Nammour S, De Moor R. [Cavity preparation using an Er:YAG laser in the adult dentition]. Rev Belge Med Dent (1984) 2009; 64:71-80. French.
Bader C, Krejci I. Indications and limitations of Er:YAG laser applications in dentistry. Am J Dent 2006;19:178-86.
Tseng WY, Chen MH, Lu HH, Lin CW, Hsieh TT, Chen CH, et al. Tensile bond strength of Er, Cr: YSGG laserirradiated human dentin to composite inlays with two resin cements. Dent Mater J 2007; 26: 746-55.
Chinelatti MA, Corona SAM, Borsatto MC, Garcia L, Ramos RP, Palma-Dibb RG. Analysis of surfaces and adhesive interfaces of enamel and dentin after different treatments. J Mater Sci: Mater Med 2007; 18:1465–70.
Ericson D. The concept of minimally invasive dentistry. Dent Update 2007;34:9-10,12-4,17-8.
Murdoch-Kinch CA, McLean ME. Minimally invasive dentistry. J Am Dent.Assoc 2003;134:87-95.
Nokhbatolfoghahaie H, Chiniforush N, Shahabi S, Monzavi A. Scanning Electron Microscope (SEM) Evaluation of Tooth Surface Irradiated by Different Parameters of Erbium: Yttrium Aluminium Garnet(Er:Yag) Laser. J Lasers Med Sci 2012; 3(2):51-5.
Souza-Zaroni WC, Chinelatti MA, Delfino CS, Pécora JD, Palma-Dibb RG, Corona SA. Adhesion of a self-etching system to dental substrate prepared by Er:YAG laser or air abrasion. J Biomed Mater Res B Appl Biomater 2008;86(2):321-9.
Ceballo L, Toledano M, Osorio R, Tay FR, Marshall GW. Bonding to Er-YAG-laser-treated dentin. J Dent Res 2002; 81: 119-22.
Trajtenberg CP, Pereira PN, Powers JM. Resin bond strength and micromorphology of human teeth prepared with an Erbium:YAG laser. Am J Dent. 2004;17: 331-6.
Van Meerbeek B, Inokoshi S, Braem M, Lambrechts P, Vanherle G. Morphological aspects of the resin–dentin interdiffusion zone with different dentin adhesive systems. J Dent Res 1992;71:1530–40.
Aoki A, Ishikawa I, Yamada T, Otsuki M, Watanabe H, Tagami J, et al. Comparison between Er:YAG laser and conventional technique for root caries treatment in vitro. J Dent Res 1998;77: 1404–14.
Martinez-Insua A, da Silva Dominguez L, Rivera FG, Santana-Penin UA. Differences in bonding to acid-etched or Er:YAG-laser-treated enamel and dentin surfaces. J Prosthet Dent 2000;84:280–8.
- Abstract Viewed: 347 times
- PDF Downloaded: 162 times