Effects of Different Surface Treatment Methods and MDP Monomer on Resin Cementation of Zirconia Ceramics an In Vitro Study
Journal of Lasers in Medical Sciences,
Vol. 6 No. 4 (2015),
2 November 2015
,
Page 174-181
Abstract
Introduction: Resin cements are generally preferred for cementation of zirconia ceramics. Resin bonding of zirconia ceramics cannot be done with the same methods of traditional ceramics because zirconia is a silica-free material. In recent years, many methods have been reported in the literature to provide the resin bonding of zirconia ceramics. The purpose of this in vitro study is to evaluate effects of different surface treatments and 10-metacryloxydecyl dihydrogen phosphate (MDP) monomer on shear bond strength between zirconia and resin cement.
Methods: 120 zirconia specimens were treated as follows: Group I: sandblasting, group II: sandblasting + tribochemical silica coating + silane, group III: sandblasting + Nd:YAG (neodymium: yttrium-aluminum-garnet) laser. One specimen from each group was evaluated under scanning electron microscope (SEM). Specimens in each group were bonded either with conventional resin cement Variolink II or with a MDP containing resin cement Panavia F2.0. Subgroups of bonded specimens were stored in distilled water (37°C) for 24 hours or 14 days. Following water storage shear bond strength test was performed at a crosshead speed of 1 mm/min in a universal test machine. Then statistical analyses were performed.
Results: Highest shear bond strength values were observed in group II. No significant difference between group I and III was found when Panavia F2.0 resin cement was used. When Variolink II resin cement was used group III showed significantly higher bond strength than group I. In group I, Panavia F2.0 resin cement showed statistically higher shear bond strength than Variolink II resin cement. In group II no significant difference was found between resin cements. No significant difference was found between specimens stored in 37°C distilled water for 24 hours and 14 days. In group I surface irregularities with sharp edges and grooves were observed. In group II less roughened surface was observed with silica particles. In group III surface microcracks connecting each other were observed.
Conclusion: Tribochemical silica coating is an effective method for achieving an acceptable bond between zirconia and resin cement. Use of a MDP monomer containing resin cement increases the bond strength of sandblasted zirconia.
- Zirconia
- Resin cement
- Bond strength.
How to Cite
References
Subaşı G, İnan Ö. Evaluation of topographical surface changes and roughness of zirconia after different surface treatments. Lasers Med Sci. 2012;27:735-742. doi:10.1007/s10103-011-0965-3
Liu L, Liu S, Song X, Zhu Q, Zhang W. Effect of Nd:YAG laser irradiation on surface properties and bond strength of zirconia ceramics. Lasers Med Sci. 2013;7:1381-1387. doi:10.1007/s10103-013-1381-7
Calvalcanti AN, Foxton RM, Watson TF, Oliveira MT, Giannini M, Marchi GM. Bond strength of resin cements to a zirconia ceramic with different surface treatments. Oper Dent. 2009;34(3):280-287. doi:10.2341/08-80
Raigrodski AJ. Contemporary materials and technologies for all- ceramic fixed partial dentures: a review of the literature. J Prosthet Dent. 2004;92:557- 562. doi:10.1016/j.prosdent.2004.09.015
Komine F, Blatz MB, Matsumura H. Current status of zirconia-based fixed restorations. J Oral Sci. 2010;52(4):531-539.
Manicone PF, Lommetti PR, Raffaelli L. An overview of zirconia ceramics: Basic properties and clinical aplications. J Dent. 2007;35:819-826.
Özkurt Z, Kazazoğlu E. Clinical success of zirconia in dental applications. J Prosthodont. 2010;19:64-68.
Gomes AL, Ramos JC, Reigo SS, Montero J, Albaladejo A. Thermocycling effect on microshear bond strength to zirconia ceramic using Er:YAG and tribochemical silica coating as surface conditioning. Lasers Med Sci. 2015;30(2):787-795. doi:10.1007/ s10103-013-1433-z
Chen C, Kleverlaan C, Feilzer AJ. Effect of an experimental zirconia-silica coating technique on microtensile bond strength of zirconia in different priming conditions. Dent Mater. 2012;28:127-134. doi:10.1016/j.dental.2012.04.020
Oba Y, Koizumi H, Nakayama D, Ishii T, Akazawa N, Matsumura H. Effect of silane and phosphate primers on the adhesive performance of a tri-n-butylborane initiated luting agent bonded to zirconia. Dent Mater J. 2014;33(2):226-232. doi:10.4012/dmj.2013-346
Akın H, Özkurt Z, Kırmalı Ö, Kazazoglu E, Ozdemir AK. Shear bond strength of resin cement to zirconia ceramic after aluminum oxide sandblasting and various laser treatments. Photomed Laser Surg. 2011; 29(12):797-802. doi:10.1089/pho.2011.3039
Erdem A, Akar GC, Erdem A, Kose T. Effect of different surface treatments on bond strength between resin cements and zirconia ceramics. Oper Dent. 2014;39 (3):118-127. doi:10.2341/12-420-l
Demir N, Subaşı MG, Öztürk N. Surface roughness and morphological changes of zirconia following different surface treatments. Photomed Laser Surg. 2012;30(6): 339-345. doi:10.1089/pho.2011.3213
Blatz MB, Sadan A, Martin J, Lang B. In vitro evaluation of shear bond strengths of resin to densly-sintered high purity zirconium oxide ceramic after long term storage and termal cycling. J Proshet Dent. 2004;91:356-62. doi:10.1016/j.prosdent.2004.02.001
Thompson JY, Stoner BR, Piascik JR, Smith R. Adhesion/cementation to zirconia and other non-silicate ceramics: where are we now? Dent Mater. 2011;27:71-82.
Cvikl B, Moser G, Wernish J, Raabe M, Gruber R, Moritz A. The impact of Er,Cr:YSGG laser on the shear strength of the bond between dentin and ceramic dependent on the adhesive material. Lasers Med Sci. 2011;27:717-722.
Ural Ç, Külünk T, Külünk Ş, Kurt M. The effect of laser treatment on bonding between zirconia ceramic surface and resin cement. Acta Odon Scan. 2010;68: 354-359. doi:10.3109/00016357.2010.514720
Akin H, Tugut F, Akin GE, Guney U, Mutaf B. Effect of Er:YAG laser application on the shear bond strength and microleakage between resin cements and Y-TZP cermic. Lasers Med Sci. 2012;27:333-338. doi:10.1007/s10103-011-0883-4
Öztoprak MO, Tozlu M, İşeri U, Ulkur F, Arun T. Effects of different application durations of scanning laser method on debonding strength of laminate veneers. Lasers Med Sci. 2012;27(4):713-716. doi:10.1007/s10103-011-0959-1
Tanaka R, Fujishima A, Shibata Y, Manabe A, Miyazaki T. Cooperation of phosphate monomer and silica modification on Zirconia. J Dent Res. 2008;87: 666-670. doi:10.1177/154405910808700705
Yun JY, Ha SR, Lee JB, Kim SH. Effect of sanblasting and various metal primers on the shear bond strength of resin cement to Y-TZP ceramic. Dent Mater. 2010; 26:650-8.
Shin YJ, Shin Y, Yi YA, et al. Evaluation of the shear bond strength of resin cement to Y-TZP ceramic after different surface treatments. Scanning. 2014;36(5):479-486. doi: 10.1002/sca.21142.
Wolfart M, Lehmann F, Wolfart S, Kern M. Durability of resin bond strength to zirconia ceramic after using different surface conditioning methods. Dent Mater. 2007;23:45-50. doi:10.1016/j.dental.2005.11.040
Papia E, Larsson C, Toit M, Steyern PV. Bonding between oxide ceramics and adhesive cement systems: a systematic review. J Biomed Mater Res B: Appl Biomater. 2013;102(2):395-413. doi:10.1002/ jbm.b.33013
Inokoshi M, Kameyema A, Munck JD, Minakuchi S, Meerbeek BV. Durable bonding to mechanically and/or chemically pre-treated dental zirconia. J Dent. 2013;41:170-9. doi:10.1016/j.jdent.2012.10.017
Amaral M, Beli R, Cesar PF, et al. The potential of novel primers and universal adhesives to bond to zirconia. J Dent. 2014;42:90-98. doi:10.1016/j. jdent.2013.11.004
Sano H, Shono T, Sonoda H, et al. Relationship between surface area for adhesion and tensile bond strength — Evaluation of a micro-tensile bond test. Dent Mater. 1994;10(4):236-240.
Zandsparsa R, Talua NA, Finkelman MD, Schaus SE. An in vitro comparison of shear bond strength of zirconia to enamel using different surface treatments. J Prosthodont. 2013;23(2):117-123. doi:10.1111/ jopr.12075
Oyagüe RC, Monticelli F, Toledano M, Osorio E, Ferrari M, Osorio R. Influence of surface treatments and resin cement selection on bonding to densely-sintered zirconium-oxide ceramic. Dent Mater. 2009; 25:172-179. doi:10.1016/j.dental.2008.05.012
Torres SMP, Borges GA, Spohr AM, Cury AA, Yadav S, Platt JA. The effect of surface treatments on the microshear bond strength of a resin luting agent and four all-ceramic systems. Oper Dent. 2009;34(4):399- 407. doi:10.2341/08-87
Xible AA, Tavarez RRJ, Araujo CR, Bonachela WC. Effect of silica coating and silanization on flexural strengths of zirconia posts: an in vitro study. J Prosthet Dent. 2006;95:224-229. doi:10.1016/j. prosdent.2005.12.010
Tsukakoshi M, Shinya A, Gomi H, Lassila LVJ, Vallittu PK, Shinya A. Effects of dental adhesive cement and surface treatment on bond strength and leakage of zirconium oxide ceramics. Dent Mater J. 2008;27(2):159-171. doi:10.4012/dmj.27.159
Della Bona A, Borba M, Benetti P, Cecchetti D. Effect of surface treatments on the bond strength of a zirconia-reinforced ceramic to composite resin. Braz Oral Res. 2007;21(1):10-15. doi:10.4012/dmj.27.159
Atsu SS, Kiliçarslan MA, Kucukesmen HC, Aka PS, Sema P Effect of zirconium-oxide ceramic surface treatments on the bond strength to adhesive resin. J Prosthet Dent. 2006;95:430-436.
Attia A. Bond strength of three luting agents to zirconia ceramic-influence of surface treatment and termocycling. J App Oral Sci. 2011;19:388-395.
Derand P, Derand T. Bond strength of luting cements to zirconium oxide ceramics. Int J Prosthodont. 2000;13(2):131-135.
Queblawi DM, Munoz CA, Brewer JD, Monaco EA Jr. The effect of zirconia surface treatment on flexural strength and shear bond strength to a resin cement. J Prosthet Dent. 2010;103:210-220.
Kern M, Wegner SM. Bonding to zirconia ceramic: adhesion methods and their durability. Dent Mater.1998; 14: 64-71. doi:10.1016/s0109- 5641(98)00011-6
Chen L, Suh BI. Bonding of resin materials to all-ceramics: a review. Curr Res Dent. 2012;3(1):7-17.
Akyıl MŞ, Uzun İH, Bayındır F. Bond strength of resin cement to yttrium-stabilized tetragonal zirconia ceramic treated with air abrasion, silica coating, and laser irradiation. Photomed Laser Surg. 2010;28(6): 801-808. doi:10.1089/pho.2009.2697
Monaco C, Cardelli P, Scotti R, Valandro LF. Pilot evaluation of four experimental conditioning treatments to improve the bond strength between resin cement and Y-TZP ceremic. J Prosthodont. 2011: 20:97-100.
Özcan M, Melo RM, Souza RO, Machado JPB, Valandro LF, Botttino MA. Effect of air-particle abrasion protocols on the biaxial flexural strength, surface characteristics and phase transformation of zirconia after cyclic loading. Journal of the Mech Behav Biomed Mater. 2013;20:19-28. doi:10.1016/j. jmbbm.2013.01.005
Spohr AM, Borges GA, Burnett Junior LH, Mota EG, Oshima HM. Surface modification of In-Ceram Zirconia ceramic by Nd:YAG laser, Rocatec system, or Aluminum oxide sandblasting and its bond strength to aresin cement. Photomed Laser Surg. 2008;26(3): 203-208. doi:10.1089/pho.2007.2130
Aboushelib MN, Wang H. Effect of surface treatment on flexural strength of zirconia bars. J Prosthet Dent. 2010;104:98-104. doi:10.1016/s0022- 3913(10)60100-x
Kosmac T, Oblak C Jevnikar P, Funduk N, Marion L. The effect of surface grinding and sandblasting on flexural strength and reliability of Y-TZP zirconia ceramic. Dent Mater. 1999;15:426-433. doi:10.1016/ s0109-5641(99)00070-6
Scherrer SS, Cattani-Laronte M, Vittecoq E, Mestral F, Griggs A, Wiskott HW. Fatigue behavior in water of Y-TZP zirconia ceramics after abrasion with 30 μm silica-coated alümina particles. Dent Mater. 2011;27: 28-42.
Üşümez A, Hamdemirci N, Köroğlu BY, et al. Bond strength of resin cement to zirconia ceramic with different surface treatments. Lasers Med Sci. 2013;28(1):259-266.
Moon J, Kim S, Lee J, Ha S, Choi Y. The effect of preparation order on the crystal structure of yitria-stabilized tetragonal zirconia polycrystals and shear bond strength of dental resin cements. Dent Mater. 2011;27:651-663. doi:10.1016/j.dental.2011.03.005
Phark J, Duarte S, Blatz M, Sadan A. An in vitro evaluation of the long-term resin bond to a new densely sintered high purity zirconium-oxide ceramic surface. J Prosthet Dent. 2009;101:29-38. doi:10.1016/ s0022-3913(08)60286-3
Subaşı G, İnan Ö. Influence of surface treatments and resin cement selection on bonding to zirconia. Lasers Med Sci. 2014;29:19-27. doi:10.1007/s10103-012- 1221-1
Kırmalı Ö, Akın H, Kapdan A. Evaluation of the surface roughness of zirconia ceramics after different surface treatments. Acta Odon Scan. 2014;72(6):432- 439. doi:10.3109/00016357.2013.853320
Shahin R, Ker, M. Effect of air abrasion on the retention of zirconia ceramic crowns luted with different cements before and after artificial aging. Dent Mater. 2010;26:922-928. doi:10.1016/j.dental.2010.06.006
Akgüngör G, Şen D, Aydın M. Influence of different surface treatments on the short term bond strength and durability between zirconia post and a composite resin core material. J Prosthet Dent. 2008;99:388-399. doi:10.1016/s0022-3913(08)60088-8
Yang B, Barloi A, Kern M. Influence of air-abrasion on zirconia ceramic bonding using an adhesive composite resin. Dent Mater. 2010;26:44-50.
Gomes AL, Oyagüe RC, Lynch CD, et al. Influence of sandblasting granulometry end resin cement composition on microtensile bond strength to zirconia ceramic for dental prosthetic frameworks. J Dent. 2013;41:31-41. doi:10.1016/j.jdent.2012.09.013
Kim M, Kim YK, Kim K, Kwon T. Shear bond strength of various luting cements to zirconia ceramic: surface chemical aspects. J Dent. 2011;39:795-803. doi:10.1016/j.jdent.2011.08.012
Kitayama S, Nikaido T, Ikeda M, Alireza S, Miura H, Tagami J. Internal coating of zirconia restoration with silica-based ceramic improves bonding of resin cement to dental zirconia ceramic. Biomed Mater Eng. 2010;20:77-87. doi:10.3233/BME-2010-0617.
Nothdurft EP, Motter PJ, Pospiech PR. Effect of surface treatment on the initial bond strength of different luting cements to zirconium oxide ceramic. Clin Oral Invest. 2009;13:229-235. doi:10.1007/ s00784-008-0222-8
Lung CY, Botelho MG, Heinonen M, Matinlinna JP. Resin zirconia bonding promotion with some novel coupling agents. Dent Mater. 2012;28:863-872. doi:10.1016/j.dental.2012.04.023
- Abstract Viewed: 1087 times
- PDF Downloaded: 410 times