Introduction: The most common causes of fiber post-failure are inadequate restorations and dislodgement. This study aimed to evaluate fiber post-bond strength to dentin following Er, Cr: YSGG laser irradiation.
Methods: A total of 65 human mandibular premolars with single roots were included. The 14 mm root length was instrumented with the rotary system using the crown-down technique. Gutta-percha was used for obturation, followed by conventional post-space preparation. The samples were divided into two major groups: control (A) and Er, Cr: YSGG (2780 nm) laser group (B). The laser group was subdivided into (B1) 1.25 W, (B2) 1.5 W, and (B3) 1.75 W. All laser groups were set at 20 Hz, 10% and 30% water/air ratio. Fiber posts were cemented with selfadhesive cement. Each sample was divided horizontally into two slices, coronal and apical. The universal testing equipment was used to conduct a push-out test. All groups were examined by SEM and temperature changes. The statistical analysis was performed by using one-way ANOVA and Tukey HSD tests.
Results: SEM images of all laser groups revealed the elimination of the smear layer and opened dentinal tubules, which was particularly noticeable in the apical region with no thermal risk to the periodontal tissue. In the push-out test, all laser groups had highly significant (P<0.001) increases in the bond strength of fiber post-to-dentin. The failure mode of the control group was a predominantly adhesive failure, whereas the laser groups were a predominantly mixed type.
Conclusion: The three laser protocols can be used safely in the surface treatment of the fiber post space of endodontically treated teeth. Laser helps to increase the bond strength of fiber post to dentin, especially in the apical area.