Shear Bond Strength of the Metal Bracket to Zirconium Ceramic Restoration Treated by the Nd: YAG Laser and Other Methods: An In Vitro Microscopic Study
Journal of Lasers in Medical Sciences,
Vol. 11 No. 4 (2020),
3 October 2020
,
Page 411-416
Abstract
Introduction: Providing reliable bonding of the bracket base and the zirconia surface is required to apply orthodontic force. The purpose of this scientific experiment was to evaluate the efficacy of three different methods of surface preparation for Zirconia, including surface roughening, sandblasting and the Nd: YAG laser, in the shear bond strength (SBS) of the orthodontic brackets.
Methods: Fifty-four discs of zirconia were divided into three groups of 18: A) Hydrofluoric acid etching, B) sandblasting, and C) Nd: irradiation using the power of 1.5 W for 10 seconds. After bonding the brackets, the samples were slowly thermo-cycled (1000 times) for 24 hours. The SBS test was performed by a universal testing machine at a head speed of 0.5 mm/min. The adhesive remnant index (ARI) was scored at a magnification of 10 in the stereo microscope. All data were collected and analyzed using the variance, Kruskal-Wallis, Tukey, Don, and Weibull tests (α = 0.05).
Results: The HF acid etching group (6.11± 0.94 MPa) had the highest SBS, which was followed by the laser group (6 ± 0.61 MPa) and the sandblast group (3.1080 ± 0.82 MPa). There was a significant statistical difference between the laser and HF groups and the sandblast group (P < 0.05) and no significant difference between the HF group and the laser group (P = 0.03).
Conclusion: Based on the obtained bond strength, the Nd: YAG laser with a power of 1.5 W could be a substitute treatment method for the HF acid-etching.
- Hydrofluoric Acid
- Laser
- Shear Strength
- Zirconium.
How to Cite
References
- Sobouti F, Rakhshan V, Chiniforush N, Khatami M. Effects of laser-assisted cosmetic smile lift gingivectomy on postoperative bleeding and pain in fixed orthodontic patients: a controlled clinical trial. Prog Orthod. 2014 Dec 9;15(1):66. doi: 10.1186/s40510-014-0066-5.
- Akova T, Yoldas O, Toroglu MS, Uysal H. Porcelain surface treatment by laser for bracket-porcelain bonding. Am J Orthod Dentofacial Orthop. 2005;128(5):630-7. doi: 10.1016/j.ajodo.2004.02.021.
- Rekow ED, Silva NR, Coelho PG, Zhang Y, Guess P, Thompson V. Performance of dental ceramics: challenges for improvements. J Dent Res. 2011;90(8):937-52. doi: 10.1177/0022034510391795.
- Manicone PF, Iommetti PR, Raffaelli L. An overview of zirconia ceramics: basic properties and clinical applications. J Dent. 2007;35(11):819-26. doi: 10.1016/j.jdent.2007.07.008.
- Visuri SR, Gilbert JL, Wright DD, Wigdor HA, Walsh Jr JT. Shear strength of composite bonded to Er:YAG laser-prepared dentin. J Dent Res. 1996;75(1):599-605. doi: 10.1177/00220345960750011401.
- Vijayaraghavan R, Rao VAP, Reddy NV, Krishnakumar R, Sugumaran DK, Mohan G. Assessment and comparison of microleakage of a fluoride-releasing sealant after acid etching and Er:YAG laser treatment – An in vitro study. Contemp Clin Dent. 2012;3(1):64-8. doi: 10.4103/0976-237X.94549.
- Yassaei S, Moradi F, Aghili H, Lotfi Kamran MH. Shear bond strength of orthodontic brackets bonded to porcelain following etching with Er:YAG laser versus hydrofluoric acid. Orthodontics (Chic). 2013;14(1):e82-7. doi: 10.11607/ortho.856.
- Raigrodski AJ, Chiche GJ, Potiket N, Hochstedler JL, Mohamed SE, Billiot S, et al. The efficacy of posterior three-unit zirconium-oxide-based ceramic fixed partial dental prostheses: A prospective clinical pilot study. J Prosthet Dent. 2006;96(4):237-44. doi: 10.1016/j.prosdent.2006.08.010.
- Zhang Y, Chai H, Lee JJW, Lawn BR. Chipping resistance of graded zirconia ceramics for dental crowns. J Dent Res. 2012;91(3):311-5. doi: 10.1177/0022034511434356.
- Sobouti F , Rakhshan V, Gholamrezaei Saravi M, Zamanian A, Shariati M. Two-year survival analysis of twisted wire fixed retainer versus spiral wire and fiber-reinforced composite retainers: a preliminary explorative single-blind randomized clinical trial. Korean J Orthod. 2016;46(2):104-10. doi: 10.4041/kjod.2016.46.2.104.
- Lee JY, Kim JS, Hwang CJ. Comparison of shear bond strength of orthodontic brackets using various zirconia primers. Korean J Orthod. 2015;45(4):164-70. doi: 10.4041/kjod.2015.45.4.164.
- Zachrisson YØ, Zachrisson BU, Büyükyilmaz T. Surface preparation for orthodontic bonding to porcelain. Am J Orthod Dentofacial Orthop. 1996;109(4):420-30. doi: 10.1016/S0889-5406(96)70124-5.
- Blakey R, Mah J. Effects of surface conditioning on the shear bond strength of orthodontic brackets bonded to temporary polycarbonate crowns. Am J Orthod Dentofacial Orthop. 2010;138(1):72-8. doi: 10.1016/j.ajodo.2008.08.030.
- Karan S, Büyükyılmaz T, Toroğlu MS. Orthodontic bonding to several ceramic surfaces: are there acceptable alternatives to conventional methods? Am J Orthod Dentofacial Orthop. 2007;132(2):144.e7-14. doi: 10.1016/j.ajodo.2006.12.006.
- Hosseini MH, Sobouti F, Etemadi A, Chiniforush N, Shariati M. Shear bond strength of metal brackets to feldspathic porcelain treated by Nd:YAG laser and hydrofluoric acid. Lasers Med Sci. 2015;30(2):837-41. doi: 10.1007/s10103-013-1458-3.
- Heravi F, Moazzami SM, Dehghani M. Effects of different surface preparations on shear bond strength of orthodontic brackets to porcelain. J Calif Dent Assoc. 2010;38(11):794-9.
- Mirhashemi A, Sharifi N, Moharrami M, Chiniforush N. Evaluation of different types of lasers in surface conditioning of porcelains: a review article. J Lasers Med Sci. 2017;8(3):101-111. doi: 10.15171/jlms.2017.19.
- Poosti M, Jahanbin A, Mahdavi P, Mehrnoush S. Porcelain conditioning with Nd:YAG and Er:YAG laser for bracket bonding in orthodontics. Lasers Med Sci. 2012;27(2):321-4. doi: 10.1007/s10103-010-0878-6.
- Hosseini MH, Sobouti F, Etemadi A, Chiniforush N, Bouraima SA. Scanning electron microscope comparative evaluation of feldspathic porcelain surfaces under irradiation by different powers of Neodymium-doped Yttrium Aluminium Garnet (Nd:YAG) laser. J Lasers Med Sci. 2013;4(2):75-8.
- Paranhos MP, Burnett LH Jr, Magne P. Effect Of Nd:YAG laser and CO2 laser treatment on the resin bond strength to zirconia ceramic. Quintessence Int. 2011;42(1):79-89.
- Kim JT, Cho SA. The effects of laser etching on shear bond strength at the titanium ceramic interface. J Prosthet Dent. 2009;101(2):101-106. doi: 10.1016/S0022-3913(09)60002-0.
- Barbosa VL, Almeida MA, Chevitarese O, Keith O. Direct bonding to porcelain. Am J Orthod Dentofacial Orthop. 1995;107(2):159-164. doi: 10.1016/s0889-5406(95)70131-1.
- Reynolds IR, von Fraunhofer JA. Direct bonding of orthodontic brackets—a comparative study of adhesives. Br J Orthod. 1976;3(3):143-146. doi: 10.1179/bjo.3.3.143.
- Murthy V, Manoharan, Balaji, Livingstone D. Effect of four surface treatment methods on the shear bond strength of resin cement to zirconia ceramics- a comparative in vitro study. J Clin Diagn Res. 2014;8(9):ZC65-8. doi: 10.7860/JCDR/2014/10104.4872.
- Kimura Y, Wilder‐Smith P, Matsumoto K. Lasers in endodontics: a review. Int Endod J. 2000;33(3):173-85. doi: 10.1046/j.1365-2591.2000.00280.x.
- Arami S, Tabatabae MH, Namdar SF, Chiniforush N. Effects of different lasers and particle abrasion on surface characteristics of zirconia ceramics. J Dent (Tehran). 2014;11(2):233-41.
- Ersu B, Yuzugullu B, Yazici AR, Canay S. Surface roughness and bond strengths of glass-infiltrated alumina-ceramics prepared using various surface treatments. J Dent. 2009;37(11):848-56. doi: 10.1016/j.jdent.2009.06.017.
- Sinha PK, Nanda RS, Duncanson MG, Hosier MJ. Bond strengths and remnant adhesive resin on debonding for orthodontic bonding techniques. Am J Orthod Dentofacial Orthop. 1995;108(3):302-7. doi: 10.1016/s0889-5406(95)70025-0.
- Fernandez L, Canut JA. In vitro comparison of the retention capacity of new aesthetic brackets. Eur J Orthod. 1999;21(1):71-7. doi: 10.1093/ejo/21.1.71.
- Lee BS, Hsieh TT, Lee YL, Lan WH, Hsu YJ, Wen PH, et al. Bond strengths of the orthodontic bracket after acid-etched, Er: YAG laser-irradiated and combined treatment on the enamel surface. Angle Orthod. 2003;73(5):565-70. doi: 10.1043/0003-3219(2003)073<0565:BSOOBA>2.0.CO;2.
- Valletta R, Prisco D, De Santis R, Ambrosio L, Martina R. Evaluation of the debonding strength of orthodontic brackets using three different bonding systems. Eur J Orthod. 2007;29(6):571-7. doi: 10.1093/ejo/cjm056.
- Schmage P, Nergiz I, Herrmann W, Özcan M. Influence of various surface-conditioning methods on the bond strength of metal brackets to ceramic surfaces. Am J Orthod Dentofacial Orthop. 2003;123(5):540-6. doi: 10.1067/mod.2003.S0889540602569110.
- Abstract Viewed: 472 times
- PDF Downloaded: 280 times