Cytotoxic Effects of Various Mineral Trioxide Aggregate Formulations, Calcium-Enriched Mixture and a New Cement on Human Pulp Stem Cells

Zahra Jaberiansari, Seddigheh Naderi, Fahime Sadat Tabatabaei




Introduction: This in vitro study compared the cytotoxic effects of three commercially available MTA formulations naming ProRoot MTA (PMTA), Angelus MTA (AMTA), and Root MTA (RMTA), with calcium-enriched mixture (CEM) cement and a new nanohybrid MTA (NMTA) on human dental pulp stem cells (DPSC). Methods and Materials: Four disc-shaped specimens of each material were prepared. After completion of setting, 2 different (neat and 1/2) elutes of the test materials were made. Then in each cavity of a 96-well plate, 3000 cells were seeded and incubated in a humidified incubator with 5% CO2 and 95% air at 37°C for 24 h. After this period, the culture medium of each well was replaced with 200 μL of test material elutes. Plain culture medium was used as the negative control and distilled water as the positive control group. Cell viability was assessed using 2, 5-diphenyl-SH-tetrazelium bromide colorimetric assay, aka Mosmann’s tetrazolium toxicity (MTT) assay, at three time intervals (24, 48, and 72 h after mixing). Data were analyzed using the ANOVA and Tukey’s post hoc test (P=0.05). Results: After 24 h, the viability of cells in neat concentration had no significant differences (P>0.05) except for the NMTA. However, CEM and AMTA, at 1/2 concentration exerted significant proliferative effects on cells. At 48 and 72-h intervals, significant proliferation of DPSCs was seen in all samples, except for the NMTA which exerted toxic effects on cells. Conclusion: All of the three commercial MTAs and CEM cement showed comparative biocompatibility. However, NMTA had cytotoxic effects on DPSCs at all the time intervals.



Angelus MTA; Calcium-Enriched Mixture; CEM Cement; Cytotoxicity; Dental Pulp Cells; Mineral Trioxide Aggregate; MTT Assay; ProRoot MTA; Root MTA; Stem Cells

DOI: https://doi.org/10.22037/iej.v9i4.5995


  • There are currently no refbacks.